Welding Instruction |
||||||||||
(1) Dry the electrodes at 100-200°C for 30-60 minutes before use. (2) Preheat temperature should be ≥ 250°C and PWHT should be 600°C. (3) Weld beads should be put down in grid shape to prevent the surfacing layers from spalling. |
||||||||||
Typical Chemical Composition of Weld Metal (wt. %) |
||||||||||
C |
Si |
Mn |
W |
Fe |
||||||
3.150 |
0.30 |
2.10 |
42.3 |
bal. |
||||||
Typical Hardness of Weld Metal |
||||||||||
Hardness Condition |
Vicker’s hardness (HV) |
Rockwell’s hardness (HRC) |
Shore’s hardness (HS) |
|||||||
Interpass temp.≤300°C |
760 |
68 |
85 |
|||||||
Continuous build-up |
645 |
67 |
77 |
|||||||
Size and Suggested Operating Range (AC or DC+) |
||||||||||
Diameter x Length(mm) |
3.2x350 |
4.0x350 |
5.0x350 |
|||||||
Amp |
90~140 |
140~190 |
190~250 |