Welding Instruction |
|||||||||||||||
(1) Dry the electrodes at 300-350°C for 30-60 minutes before use. (2) Preheat temperature should be ≥ 250°C and PWHT should be 600°C. (3) The surfacing should be limited to 2-3 layers.
|
|||||||||||||||
Typical Chemical Composition of Weld Metal (wt. %) |
|||||||||||||||
C |
Si |
Mn |
Cr |
||||||||||||
3.950 |
1.07 |
2.65 |
25.25 |
||||||||||||
Typical Hardness of Weld Metal |
|||||||||||||||
Hardness Condition |
Vicker’s hardness (HV) |
Rockwell’s hardness (HRC) |
Shore’s hardness (HS) |
||||||||||||
As-welded |
Interpass temp. ≤100°C |
660 |
58 |
79 |
|||||||||||
Continuous build-up |
630 |
56 |
77 |
||||||||||||
Heat treatment |
Temperature (°C) |
200 |
300 |
400 |
500 |
600 |
700 |
||||||||
Vicker’s hardness |
640 |
460 |
400 |
300 |
180 |
100 |
|||||||||
Size and Suggested Operating Range (AC or DC+) |
|||||||||||||||
Diameter x Length(mm) |
3.2x350 |
4.0x350 |
5.0x350 |
||||||||||||
Amp |
90~140 |
140~190 |
190~250 |