Welding Instruction |
|||||||||||||
(1) Dry the electrodes at 300-350°C for 30-60 minutes before use. ( 2 ) Preheat temperature should be ≥ 300°C and slow cooling after welding is required. ( 3 ) Recommended heat treatment: Quench…..1200~1250°C oil quenching. Temper…..540~570°C air cooling. |
|||||||||||||
Typical Chemical Composition of Weld Metal (wt. %) |
|||||||||||||
C |
Si |
Mn |
Cr |
Mo |
V |
W |
|||||||
1.050 |
1.05 |
0.21 |
4.65 |
9.15 |
1.82 |
4.21 |
|||||||
Typical Hardness of Weld Metal |
|||||||||||||
Hardness Condition |
Vicker’s hardness (HV) |
Rockwell’s hardness (HRC) |
Shore’s hardness (HS) |
||||||||||
As-welded |
Interpass temp. ≤150°C |
743 |
62 |
84 |
|||||||||
Continuous build-up |
682 |
59 |
80 |
||||||||||
Heat treatment |
1200~1250°C oil quench |
783 |
63 |
87 |
|||||||||
540~570°C air cooling |
|||||||||||||
Size and Suggested Operating Range (AC or DC+) |
|||||||||||||
Diameter x Length(mm) |
3.2x350 |
4.0x350 |
5.0x350 |
6.0X400 |
|||||||||
Amp |
80~120 |
120~170 |
160~210 |
200~280 |