Welding Instruction |
||||||||||||
(1) Dry the electrodes at 200-250°C for 30-60 minutes before use. (2) Preheat temperature should be above 200°C. Use slow cooling and stress relieving after welding.
|
||||||||||||
Typical Chemical Composition of Weld Metal (wt. %) |
||||||||||||
C |
Si |
Mn |
Cr |
|||||||||
0.200 |
0.40 |
0.20 |
11.50 |
|||||||||
Typical Hardness of Weld Metal |
||||||||||||
Hardness Condition |
Vicker’s hardness (HV) |
Rockwell’s hardness (HRC) |
Shore’s hardness (HS) |
|||||||||
As-welded |
Interpass temp. ≤150°C |
528 |
51 |
68 |
||||||||
Continuous build-up |
510 |
50 |
67 |
|||||||||
Work-hardened |
630 |
56 |
75 |
|||||||||
High Temp. |
Temperature (°C) |
200 |
300 |
400 |
||||||||
Vicker`s hardness |
470 |
410 |
300 |
|||||||||
Size and Suggested Operating Range (AC or DC+) |
||||||||||||
Diameter x Length(mm) |
3.2x350 |
4.0x350 |
5.0x350 |
6.0x400 |
||||||||
Amp |
70~120 |
100~170 |
160~220 |
200~280 |