Welding Instruction
|
|
||||||||||||||
(1) Clean up the contaminations on the steel before welding.
(2) It provides high hardenability with air cooling. Preheat and PWHT are required.
(3) Preheat and interpass temperature are: 160~190°C, PWHT: 840~870°C.
|
|
||||||||||||||
TypicalChemical Composition of Weld Metal (wt %)
|
|
||||||||||||||
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
|||||||||
0.075
|
0.32
|
0.55
|
0.015
|
0.014
|
5.50
|
0.55
|
|||||||||
TypicalMechanical Properties of Weld Metal (PWHT:850°Cx2Hr)
|
|
||||||||||||||
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
|
|||||||||||
°C
|
J (kgf -m)
|
|
|||||||||||||
630(64.2)
|
480(49.0)
|
25
|
0
|
—
|
|
||||||||||
-120
|
—
|
|
|||||||||||||
Size and SuggestedOperating Range (DC+)
|
|
||||||||||||||
Diameter (mm)
Parameters
|
1.0
|
1.2
|
1.4
|
1.6
|
|
||||||||||
Short-Circuit Transfer
|
A
|
80~160
|
100~210
|
—
|
—
|
|
|||||||||
V
|
16~22
|
17~22
|
—
|
—
|
|
||||||||||
Spray Transfer
|
A
|
180~280
|
200~300
|
210~320
|
220~330
|
|
|||||||||
V
|
24~30
|
24~30
|
24~32
|
24~32
|
|