Welding Position
|
|
||||||||||||||
All Positions
|
|
||||||||||||||
Welding Instruction
|
|
||||||||||||||
(1) Clean up the contaminations on the steel before welding.
(2) Dry the electrodes at 300~350°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A).
(4) The preheat temperature for thick plate (thickness > 25mm) or rigid joints is 90~120°C.
|
|
||||||||||||||
TypicalChemical Composition of Weld Metal (wt %)
|
|
||||||||||||||
C
|
Si
|
Mn
|
P
|
S
|
Cu
|
Cr
|
Ni
|
|
|||||||
0.060
|
0.54
|
0.84
|
0.014
|
0.009
|
0.48
|
0.52
|
0.61
|
|
|||||||
TypicalMechanical Properties of Weld Metal
|
|
||||||||||||||
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
|
|||||||||||
°C
|
J (kgf -m)
|
|
|||||||||||||
630(64.2)
|
550(56.1)
|
27
|
-5
|
104(10.6)
|
|
||||||||||
-18
|
95(9.7)
|
|
|||||||||||||
Size and SuggestedOperating Range (AC or DC+)
|
|
||||||||||||||
Diameter (mm) x Length(mm)
|
2.6x300
|
3.2x350
|
4.0x400
|
5.0x400
|
|||||||||||
Amp
|
H
|
70~100
|
110~150
|
160~200
|
180~230
|
||||||||||
V-up/OH
|
60~90
|
90~130
|
130~170
|
140~180
|