Welding Position |
|||||||||||||||
All Positions |
|||||||||||||||
Welding Instruction |
|||||||||||||||
(1) Clean up the contaminations on the steel. (2) Dry the electrodes at 350~400°C for 60 minutes before welding. (3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A). (4) High heat input will lower the impact value. Please carefully select the welding current. (5) The preheat temperature for thick plate is 90~120°C. |
|||||||||||||||
Typical Chemical Composition of Weld Metal (wt %) |
|||||||||||||||
C |
Si |
Mn |
P |
S |
Ni |
|
|||||||||
0.070 |
0.62 |
0.90 |
0.013 |
0.012 |
1.02 |
|
|||||||||
Typical Mechanical Properties of Weld Metal (As welded) |
|||||||||||||||
Tensile Strength N/mm2(kgf/mm2) |
Yield Strength N/mm2(kgf/mm2) |
Elongation % |
Charpy V-Notch |
||||||||||||
°C |
J (kgf -m) |
||||||||||||||
560(57.1) |
470(48.0) |
29 |
-40 |
128(13.1) |
|||||||||||
-45 |
118(12.0) |
||||||||||||||
Size and Suggested Operating Range (AC or |
|||||||||||||||
Diameter (mm) x Length(mm) |
2.6x300 |
3.2x350 |
4.0x400 |
5.0x400 |
|
||||||||||
Amp |
H |
70~100 |
100~140 |
140~180 |
180~230 |
|
|||||||||
V-up/OH |
60~90 |
90~130 |
120~160 |
— |
|