| Product name：KN-816G |
| Classification：A5.5 / E8016-G |
  |
- It is suitable for welding 540N/mm2 grade steel for low temperature resistance.
- It provides good weldability, stable arc and easy slag removal.
- Weld metal contains 1.5%Ni and has good impact properties at -45°C.
- It is ideal for welding low temperature steel used in LPG storage tanks, such as ASTM A537C1, JIS G3126 and SLA325A.
|
Welding Position
|
|||||||||||||||
|
All Positions
|
|||||||||||||||
|
Welding Instruction
|
|||||||||||||||
|
(1) Clean up the contaminations on the steel.
(2) Dry the electrodes at 350~400°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A)
(4) High heat input will lower the impact value. Please carefully select the welding current.
(5) The preheat temperature for thick plate is 50~100°C.
|
|||||||||||||||
|
TypicalChemical Composition of Weld Metal (wt %)
|
|||||||||||||||
|
C
|
Si
|
Mn
|
P
|
S
|
Ni
|
|
|||||||||
|
0.080
|
0.87
|
1.10
|
0.011
|
0.010
|
1.54
|
|
|||||||||
|
TypicalMechanical Properties of Weld Metal (PWHT:745°Cx1Hr)
|
|||||||||||||||
|
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
||||||||||||
|
°C
|
J (kgf -m)
|
||||||||||||||
|
565(57.6)
|
480(49.0)
|
32
|
0
|
—
|
|||||||||||
|
-45
|
89(9.1)
|
||||||||||||||
|
Size and SuggestedOperating Range (AC or DC+)
|
|||||||||||||||
|
Diameter (mm) x Length(mm)
|
2.6x300
|
3.2x350
|
4.0x400
|
5.0x400
|
|||||||||||
|
Amp
|
H
|
70~100
|
100~140
|
140~180
|
180~230
|
||||||||||
|
V-up/OH
|
60~90
|
90~130
|
120~160
|
—
|
|||||||||||