Welding Position
|
|||||||||||||
All Positions
|
|||||||||||||
Welding Instruction
|
|||||||||||||
(1) Clean up the contaminations on the steel.
(2) Dry the electrodes at 350~400°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A)
(4) Preheat and interpass temperature: 177~232°C, PWHT: 725~755°C.
|
|||||||||||||
TypicalChemical Composition of Weld Metal (wt %)
|
|||||||||||||
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
|||||||
0.052
|
0.29
|
0.47
|
0.015
|
0.014
|
5.57
|
0.57
|
|||||||
TypicalMechanical Properties of Weld Metal (PWHT:745°Cx1Hr)
|
|||||||||||||
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
||||||||||
°C
|
J (kgf -m)
|
||||||||||||
580(59.0)
|
410(42.0)
|
25
|
0
|
—
|
|||||||||
-29
|
—
|
||||||||||||
Size and SuggestedOperating Range (AC or DC+)
|
|||||||||||||
Diameter (mm) x Length(mm)
|
3.2x350
|
4.0x400
|
5.0x400
|
||||||||||
Amp
|
F
|
80~120
|
100~170
|
160~230
|
|||||||||
V-up/OH
|
70~110
|
100~150
|
—
|