| Product name：KL-818B2 |
| Classification：A 5.5 / E8018-B2 |
  |
- KL-818B2 is suitable for welding Cr-Mo alloy steel.
- It provides high deposition rate and good weldability.
- Weld metal contains 1.25%Cr-0.5%Mo.
- It is ideal for welding in high pressure steel pipes, heat exchanger steel pipes, rolled, cast and forged steel, such as ASTM A387Gr.11 and JIS SCMV3.
|
Welding Position
|
||||||||||||||
|
All Positions
|
||||||||||||||
|
Welding Instruction
|
||||||||||||||
|
(1) Clean up the contaminations on the steel.
(2) Dry the electrodes at 350~400°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A)
(4) Preheat and interpass temperature: 160~190°C, PWHT: 675~705°C.
|
||||||||||||||
|
TypicalChemical Composition of Weld Metal (wt %)
|
||||||||||||||
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
||||||||
|
0.080
|
0.68
|
0.75
|
0.013
|
0.008
|
1.28
|
0.53
|
||||||||
|
TypicalMechanical Properties of Weld Metal(PWHT:690°Cx1Hr)
|
||||||||||||||
|
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
|||||||||||
|
°C
|
J (kgf -m)
|
|||||||||||||
|
640(65.3)
|
560(57.1)
|
26
|
0
|
—
|
||||||||||
|
-29
|
—
|
|||||||||||||
|
Size and SuggestedOperating Range (AC or DC+)
|
||||||||||||||
|
Diameter (mm) x Length(mm)
|
3.2x350
|
4.0x400
|
5.0x400
|
|||||||||||
|
Amp
|
F
|
90~140
|
140~190
|
180~240
|
||||||||||
|
V-up/OH
|
80~120
|
120~160
|
—
|
|||||||||||