| Product name：KL-816B1 |
| Classification：A5.5 / E8016-B1 |
  |
- KL-816B1 is suitable for welding Cr-Mo alloy steel.
- Weld metal contains 0.5%Cr-0.5%Mo.
- It is ideal for welding boilers, petro-chemical plants, forged steel and alloy steel, such as ASTM A387Gr.2, JIS SCMV 1.
|
Welding Position
|
|
|||||||||||||
|
All Positions
|
|
|||||||||||||
|
Welding Instruction
|
|
|||||||||||||
|
(1) Clean up the contaminations on the steel.
(2) Dry the electrodes at 350~400°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A)
(4) Preheat and interpass temperature: 160~190°C, PWHT: 675~705°C.
|
|
|||||||||||||
|
TypicalChemical Composition of Weld Metal (wt %)
|
|
|||||||||||||
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
||||||||
|
0.070
|
0.45
|
0.80
|
0.013
|
0.008
|
0.54
|
0.50
|
||||||||
|
TypicalMechanical Properties of Weld Metal(PWHT:690°Cx1Hr)
|
|
|||||||||||||
|
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
|||||||||||
|
°C
|
J (kgf -m)
|
|||||||||||||
|
620(63.2)
|
550(56.1)
|
30
|
0
|
—
|
||||||||||
|
-29
|
—
|
|||||||||||||
|
Size and SuggestedOperating Range (AC or DC+)
|
|
|||||||||||||
|
Diameter (mm) x Length(mm)
|
3.2x350
|
4.0x400
|
5.0x400
|
|
||||||||||
|
Amp
|
F
|
90~140
|
140~190
|
180~240
|
|
|||||||||
|
V-up/OH
|
80~120
|
120~160
|
—
|
|
||||||||||