Welding Position
|
||||||||||||
All Positions
|
||||||||||||
Welding Instruction
|
||||||||||||
(1) Clean up the contaminations on the steel.
(2) Dry the electrodes at 350~400°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A).
(4) Preheat and interpass temperature: 100~200°C, PWHT: 600~635°C.
|
||||||||||||
TypicalChemical Composition of Weld Metal (wt %)
|
||||||||||||
C
|
Si
|
Mn
|
P
|
S
|
Mo
|
|||||||
0.070
|
0.50
|
0.70
|
0.013
|
0.012
|
0.54
|
|||||||
TypicalMechanical Properties of Weld Metal(PWHT:620°Cx1Hr)
|
||||||||||||
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
|||||||||
°C
|
J (kgf -m)
|
|||||||||||
570(58.1)
|
490(50.0)
|
30
|
0
|
—
|
||||||||
-29
|
—
|
|||||||||||
Size and SuggestedOperating Range (AC or DC+)
|
||||||||||||
Diameter (mm) x Length(mm)
|
3.2x350
|
4.0x400
|
5.0x400
|
|||||||||
Amp
|
F
|
140~190
|
180~240
|
230~300
|
||||||||
V-up/OH
|
120~160
|
—
|
—
|