KS-317L - 廣泰金屬工業股份有限公司｜KUANG TAI METAL INDUSTRIAL CO., LTD.

_MG_4993

KS-317L

Type of coating: Lime titania type
Weld metal is 19%Cr-12%Ni-3%Mo, which is suitable for welding AISI 317L steel.
It is ideal for welding critical chemical vessels for sulfuric and sulphurous acid.

Catalog Packaging

▎Classification

AWS A 5.4	E317L-16
JIS Z3221	ES317L-16
EN 3581-A	–
GB T983	E317L-16

▎Applications and Features

Weld metal is 19%Cr-12%Ni-3%Mo, which is suitable for welding AISI 317L steel.
It provides good corrosion and heat resistance due to its low C and additional Mo content.
It has good strength at high temperature and post weld heat treatment is not required.
It is ideal for welding critical chemical vessels for sulfuric and sulphurous acid.

▎Welding Position

焊接姿勢

焊接姿勢

焊接姿勢

焊接姿勢

焊接姿勢

焊接姿勢

焊接姿勢

焊接姿勢

銲接姿勢

銲接姿勢

焊接姿勢

焊接姿勢

▎Welding Instruction

Please refer to Appendix H for re-drying instructions.
For other instruction information, please refer to Appendix F

▎Application

Weld metal is 19%Cr-12%Ni-3%Mo, which is suitable for welding AISI 317L steel.

▎Typical Chemical Composition of Weld Metal (wt. %)

C	Si	Mn	P	S	Cr	Ni	Mo
0.034	0.36	1.49	0.015	0.010	19.61	13.85	3.52

▎Typical Mechanical Properties of Weld Metal

Tensile Strength N/mm²	Yield Strength N/mm²	Elongation %	5% Sulfuric Acid Corrosion Test (g/m2 hr)
580	430	41	≦5

▎Size and Suggested Operating Range (AC or DC+)

Diameter(mm)	2.0	2.6	3.2	4.0	5.0
F/H-Fillet	35-55	50-85	80-120	100-150	140-200
V-up/OH	30~50	45-85	70-110	90-135	–

▎Certification

JISZ3323_TCTW08007

KUANG TAI METAL INDUSTRIAL CO., LTD.

廣泰金屬工業股份有限公司

No.20, Gongye Rd., Erzhen, Guantian Dist.
Tainan City 72042, Taiwan
TEL：886-6-6987615 FAX：886-6-6987315

Catalog Recruit