KH-13MN - 廣泰金屬工業股份有限公司｜KUANG TAI METAL INDUSTRIAL CO., LTD.

_MG_4993

KH-13MN

Type of coating: Low hydrogen type
Weld metal is an austenite structure with 13%Mn-4%Ni and provides excellent crack resistance.

Catalog Packaging

▎Classification

AWS A5.13	EFeMn-A
JIS Z3251	DFMB-400-B
EN 14700	–
GB T984	–

▎Applications and Features

Weld metal is an austenite structure with 13%Mn-4%Ni and provides excellent crack resistance.
It provides good machining properties, good work-hardening properties, good toughness and good resistance to abrasion accompanied by heavy impact.
It is suitable for repairing crusher cones and studding of 13%Mn cast steel.

Crusher Cone

Crusher Cone

▎Welding Position

焊接姿勢

焊接姿勢

焊接姿勢

焊接姿勢

▎Welding Instruction

Dry the electrodes at 300-350°C for 30-60 minutes before use.
Preheat is not needed. Use low current to prevent overheat.
Keep good ventilation during welding.

▎Applications

It is suitable for repairing crusher cones and studding of 13%Mn
cast steel.

▎Typical Chemical Composition of Weld Metal (wt.%)

C	Si	Mn	Ni
0.68	0.50	13.51	3.71

▎Typical Hardness of Weld Metal

Condition	Vicker’s hardness (HV)	Rockwell’s hardness (HRC)	Shore’s hardness (HS)
Interpass temp.≤150°C	190	8.5	28
Work-hardened	430	43	58

▎Size and Suggested Operating Range (AC or DC+)

Diameter x Length(mm)	3.2×350	4.0×400	5.0×400
Amp	90-140	140-190	190-250

▎Certification

JISZ3323_TCTW08007