KCH-17-SX and KF-810 are a submerged arc flux-cored wire and a flux which produces a low carbon, low alloy weld deposit with a typical hardness of 35 HRC.

Catalog Packaging

▎Classification

AWS –	–
JIS –	–
EN 14700	UP3-GF-350-P
GB –	–

▎Applications and Features

KCH-17-SX and KF-810 are a submerged arc flux-cored wire and a flux which produces a low carbon, low alloy weld deposit with a typical hardness of 35 HRC.
It provides not only good metal-to-metal abrasion resistance but also good resistance to compression and cold work deformation. The impact resistance is excellent and the crack susceptibility is low.
There is no hot crack for multi-layer build-up up to 20 mm.
The weld metal can be machined and cut after welding.
It is suitable for repairing crane wheels, idlers and mine car wheels.

▎Welding Position

▎Welding Instruction

The hardness of weld metal will decrease when the temperature of stress relief exceeds 480°C.
The preheat and interpass temperature should be controlled between 200-400°C for massive work pieces and high curvature surface to prevent weld cracking caused by high stress.

▎Applications

It is suitable for repairing crane wheels, idlers and mine car wheels.

▎Typical Chemical Composition of Weld Metal (wt.%)

C	Si	Mn	Cr	Mo
0.08	0.60	2.60	3.0	0.8

▎Typical Hardness of Weld Metal

	1st layer	2nd layer	3rd layer
Hardness(HRC)	26-30	30-35	34-38

▎Size and Suggested Operating Range (DC+)

Size (mm)	Voltage (V)	Current(A)	ESO(mm)
3.2	30-32	380-400	25-30

▎Classification

JISZ3323_TCTW08007