KH-CRX

Type of coating: Special type
Weld metal contains complex carbide precipitates of Cr, Nb, Mo, W, and V.

Weld metal contains complex carbide precipitates of Cr, Nb, Mo, W, and V.
It has the best resistance to high temperature abrasion and earth abrasion. The abrasion resistance is exceptional in high temperature corrosive conditions.
It provides stable arc and almost no slag.
The service temperature can be up to 650°C. It is suitable for repairing the parts of sintering factory, blast furnace, cement plant and agricultural machines in severe earth abrasion.

Crusher wheel

Cane knives

Dry the electrodes at 100-200°C for 30-60 minutes before use.
Preheat temperature should be ≥ 250°C and PWHT should be 600°C.
Weld beads should be put down in grid shape to prevent the surfacing layers from spalling.

It is suitable for repairing the parts of sintering factory, blast furnace, cement plant and agricultural machines in severe earth abrasion.

C	Si	Mn	Cr	Mo	Nb	V	W
5.53	1.95	1.32	24.64	5.65	6.92	1.63	1.97

Condition	Vicker’s hardness (HV)	Rockwell’s hardness (HRC)	Shore’s hardness (HS)
Interpass temp.≤300°C	1010	67	93

Diameter x Length(mm)	3.2×350	4.0×350	5.0×350
Amp	90-140	140-190	190-250

JISZ3323_TCTW08007