KL-816B2

Type of coating: Low hydrogen type
KL-816B2 is suitable for welding Cr-Mo alloy steel.

KL-816B2 is suitable for welding Cr-Mo alloy steel.
Weld metal contains 1.25%Cr-0.5%Mo.
It provides great creep resistance at 450°C.
It is ideal for welding high pressure steel pipes, heat exchanger steel pipes of boilers, rolled, cast
and forged steel。

Clean up the contaminations on the steel.
Dry the electrodes at 350~400°C for 60 minutes before welding.
Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A)
Preheat and interpass temperature: 160~190°C, PWHT: 675~705°C.

It is ideal for welding high pressure steel pipes, heat exchanger steel pipes of boilers, rolled, cast and forged steel。

C	Si	Mn	P	S	Cr	Mo
0.08	0.46	0.64	0.015	0.010	1.28	0.53

PWHT	Tensile Strength N/mm²	Yield Strength N/mm²	Elongation %
690℃ 1Hr	630	540	28

JISZ3323_TCTW08007